Select your fitting and find the right compound for your intend
PRECITE®
P3 GK 30 natural (7643)
PBT GK30
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
3.900MPa
50MPa
25kJ/m²
PRECITE® P3 GK 30 natural (7643) is a 30% glass bead filled poly(butylene terephthalate) (PBT) with excellent dimensional stability, low warpage and high surface quality.
PRECITE®
V GF 30 2 black (7724)
PBT+ASA GF30
PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.
9.500MPa
130MPa
60kJ/m²
PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.
AKROMID®
C3 GF 35 5 XTC black (5552)
PA66+PA6 GF35
AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.
11.000MPa
200MPa
100kJ/m²
AKROMID® C3 GF 35 5 XTC black (5552) is a 35% glass fibre reinforced, high heat stabilised polyamid 66/6 blend with high stiffness and strength and with extra high temperature tolerance.
AKROMID®
B28 GF 30 9 natural (6614)
PA6 GF30
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
95kJ/m²
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 50 9 natural (6570)
PA6 GF50
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
17.000MPa
250MPa
115kJ/m²
AKROMID® B28 GF 50 9 natural (6570) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength, improved mold release
AKROMID®
C3 GF 35 5 XTC black (6680)
PA66+PA6 GF35
AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking
11.500MPa
200MPa
105kJ/m²
AKROMID® C3 GF 35 5 XTC black (6680) - PA6.6/6 blend, 35% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry, laser marking
PRECITE®
P1 natural (7010)
PBT
PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.
2.400MPa
55MPa
180kJ/m²
PRECITE® P1 natural (7010) - PBT, unreinforced, low viscosity, good dimensional stability, automotive, E&E, appliances industries.
AKROMID®
AKROMID® B3 GF 15 1 L natural (4690) is a PA6/PP-blend with reduced density compared to standard PA6 with 15% glass fibre reinforcement. The material is suitable for components with average strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMID® B3 GF 15 1 L natural (4690) is particularly superior to calcium chloride (CaCl₂).
Features
Properties
5.200MPa
110MPa
60kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.