T5 GF 40 black (6486)

PPA GF40

AKROMIDĀ® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

14.500MPa

Strength

245MPa

Impact

80kJ/mĀ²

AKROMIDĀ® T5 GF 40 black (6486) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

PRECITEĀ®

Preliminary

P3 ICF 40 black (6949)

PBT CF 40

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

31.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 ICF 40 black (6949) - PBT, 40% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITEĀ®

Preliminary

E GF 30 natural (7303)

PET GF 30

PRECITEĀ® E GF 30 natural (7303) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

10.600MPa

Strength

175MPa

Impact

48kJ/mĀ²

PRECITEĀ® E GF 30 natural (7303) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

B3 GF 30 1 black (20000)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

Modulus

9.500MPa

Strength

175MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 black (20000) - 30% glass fiber reinforced PA 6, heat stabilised for technical parts in industrial engineering, automotive and agricultural machinery industry

AKROMIDĀ®

C28 GF 25 FRT grey (7530)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (7530) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 65 00, Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

NA

AKROMIDĀ® C28 GF 25 FRT grey (7530) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 65 00, Public Transportation EN 45545-2.

PRECITEĀ®

Preliminary

E GF 50 black (7395)

PET GF50

PRECITEĀ® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

Modulus

18.000MPa

Strength

210MPa

Impact

60kJ/mĀ²

PRECITEĀ® E GF 50 black (7395) - PET, 50% glass fibre, very high stiffness, very high toughness, elevated temperature, good surface, dimensional stability, metal replacement, automotive, E&E, household.

AKROMIDĀ®

C28 GF 25 FRT grey (7560)

PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

Modulus

11.000MPa

Strength

135MPa

Impact

60kJ/mĀ²

AKROMIDĀ® C28 GF 25 FRT grey (7560) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 000 35 00,Public Transportation EN 45545-2.

118192080

AKROMIDĀ®

C3 GF 30 5 XTC black (4686)PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 5 XTC black (4686) is a 30% glass fiber reinforced, high heat stabilised polyamide 6.6/6 blend. It is characterised by high stiffness and strength as well as by excellent temperature resistance. It is therefore perfectly suitable for parts in industrial engineering and in the automotive industry, which are exposed to high temperatures.

Features

heat stabilised 230

Properties

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9500 MPa
5500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
6,0 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
14 kJ/mĀ²
23 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
245 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
210 - 230 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,36 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more