AKROMID®
NEXT B3 GF 30 1 L CR black (8313)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
C28 GF 25 FRT grey (8133)
PA-Blend
AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
11.000MPa
150MPa
NA
AKROMID® C28 GF 25 FRT grey (8133) - PA blend, 25% glass fiber, flame retardant, good flowability, RAL 7011, Public Transportation EN 45545-2.
AKROLOY®
PA ICF 30 black (5269)
PA66+PA6I/6T CF30
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
25.000MPa
220MPa
50kJ/m²
AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMID®
B28 GF 30 9 natural (6614)
PA6 GF30
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
10.300MPa
185MPa
95kJ/m²
AKROMID® B28 GF 30 9 natural (6614) - PA 6, 30% glassfiber reinforced, easy flow, good surface, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 1 PST black (6647)
PA6 GF30
AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®
10.300MPa
185MPa
95kJ/m²
AKROMID® B3 GF 30 1 PST schwarz (6647) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high rigidity and strength and optimized for adhesion to PST (Plasma Seal-Tight®) coatings developed by Plasmatreat®
PRECITE®
P3 ICF 30 black (6948)
PBT CF 30
PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
23.500MPa
175MPa
50kJ/m²
PRECITE® P3 ICF 30 black (6948) - PBT, 30% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
PRECITE®
P1 GF 30 natural (7062)
PBT GF30
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
9.800MPa
150MPa
75kJ/m²
PRECITE® P1 GF 30 natural (7062) is a 30% glass fibre reinforced, low viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
AKROMID®
B3 1 L black (4525)PA6+PP
AKROMID® B3 1 L black (4525) is an unreinforced PA6-PP-blend with reduced density compared to standard PA6. The material can be used where weight and cost reduction is required.
Features
Properties
2.300MPa
55MPa
180kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at yield
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Ball indentation hardness
ISO 2039-1
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
Flowability
AKRO
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.