HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

PRECITE®

Preliminary

P3 ICF 10 black (6946)

PBT CF10

PRECITE® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

7.500MPa

Strength

100MPa

Impact

30kJ/m²

PRECITE® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITE®

Preliminary

P3 natural (7009)

PBT

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMID®

B28 GF 15 2 black (7060)

PA6 GF15

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

Modulus

6.100MPa

Strength

108MPa

Impact

32kJ/m²

AKROMID® B28 GF 15 2 black (7060) - 15% glass fibre reinforced, heat- and UV-stabilised, easy flowing polyamide 6, average stiffness and strength, passes ISO 4892-2 with 1200h exposure time.

118192080

AKROLOY®

PA GF 50 black (2706)PA66+PA6I/6T GF50

AKROLOY® PA GF 50 black (2706) is a 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 black (6507) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Properties

Modulus

17.500MPa

Strength

250MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17500 MPa
16500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
16400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
380 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
105 kJ/m²
100 kJ/m²
95 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
17 kJ/m²
17 kJ/m²
15 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
290 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
225 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
245 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
243 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,15 10⁻⁴/K
0,65 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
140 - 150 °C
110 - 130 °C

Vicat softening temperature B50

ISO 306

50°C/50N
242 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
700 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,59 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,05 %

Water absorption

ISO 62

23°C, saturated
3,5 - 4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1017 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Permittivity

IEC 60250

1 MHz
4,42

Rheological Properties

MVR

ISO 1133

275°C/5kg
9 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.