AKROMID®

B3 ICF 40 AM black (8236)

PA6 CF40

AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

Modulus

27.000MPa

Strength

210MPa

Impact

45kJ/m²

AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

AKROMID®

Preliminary

B25 GF 40 L black (8452)

PA6+PP GF40

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

Modulus

11.500MPa

Strength

150MPa

Impact

60kJ/m²

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

AKROMID®

B3 GF 30 S1 LA black (4446)

PA6-I GF30

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

Modulus

8.400MPa

Strength

150MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 LA black (4446) - PA 6, 30% glass fiber reinforced, impact modified, laser markable, housings, covers, automotive

AKROMID®

B3 GF 45 1 black (5744)

PA6 GF45

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.000MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (5744) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

PRECITE®

Preliminary

P3 ICF 10 black (6946)

PBT CF10

PRECITE® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

7.500MPa

Strength

100MPa

Impact

30kJ/m²

PRECITE® P3 ICF 10 black (6946) - PBT, 10% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITE®

Preliminary

P3 natural (7009)

PBT

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE® P3 natural (7009) - PBT, unreinforced, medium viscosity, good dimensional stability, automotive, E&E, appliances industries.

AKROMID®

Preliminary

B3 GFM 20/30 1 black (7677)

PA6 (GF20+MD30)

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

Modulus

14.000MPa

Strength

145MPa

Impact

45kJ/m²

AKROMID® B3 GFM 20/30 1 black (7677) is a 20% glass fibre reinforced and 30% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability.

115161780

AKROMID®

Preliminary

B3 GF 40 S1 black (8647)PA6-I GF40

EXPERIMENTAL GRADE AKROMID® B3 GF 40 S1 black (8647) is a 40% glass fiber reinforced, impact modified polyamide 6. It is characterised by a high cold impact a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Features

impact modified
reduced density

Properties

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
105 kJ/m²
125 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
26 kJ/m²
38 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,42 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0.25 - 0.45 %
0.7 - 0.9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
100 mm
310 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more