AKROMID®

S3 8 natural (4881)PA610

AKROMID® S3 8 natural (4881) is an unreinforced polyamide 6.10 with lower moisture absorption, high chemical resistance and light inherent color, modified for the respective application.

Features

reduced moisture
sustainable

Regulatory

eu102011fda

Properties

Modulus

2.300MPa

Strength

65MPa

Impact

180kJ/m²

Sustainability

Biobased carbon content

56 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
65 MPa
50 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 75 %
> 75 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
4 kJ/m²
12 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
55 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

General Properties

Density

ISO 1183

23°C
1,08 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
1,6 %
1,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

S3 1 black (3317)

PA610

AKROMID® S3 1 black (3317) is a nonreinforced and heat stabilised polyamide 6.10 with lower moisture absorption and high chemical resistance.

Modulus

2.400MPa

Strength

70MPa

Impact

180kJ/m²

AKROMID®

UL
Preliminary

NEXT S3 GF 15 1 HU natural (8822)

PA6.10 GF15

AKROMID® NEXT S3 GF 15 1 HU natural (8822) is a partially biobased and heat-stabilised PA6.10. With 15% glass fibre reinforcement, the material is suitable for household and industrial applications with medium demands on strength and stiffness. This

Modulus

5.000MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID®

UL

NEXT S3 GF 30 1 HU natural (8824)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 natural (8824) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This susta

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

PRECITE®

P1 natural (7010)

PBT

PRECITE® P1 natural (7010) is an unreinforced PBT with excellent dimensional stability and high flowability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic condit

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE®

Preliminary

P3 8 natural (7517)

PBT

PRECITE® P3 8 natural (7517) is an unreinforced polybutylene terephthalate (PBT) with medium viscosity and good dimensional stability. It is particularly suitable for precision parts in cosmetic, food contact, E/E and appliances industries.

Modulus

2.400MPa

Strength

55MPa

Impact

180kJ/m²

PRECITE®

Preliminary

P1 4 natural (8814)

PBT

PRECITE® P1 4 natural (8814) is an unreinforced, high flow PBT with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing climatic conditions. I

Modulus

2.600MPa

Strength

60MPa

Impact

NA

AKROMID®

UL

NEXT S3 GF 30 1 HU black (8825)

PA6.10 GF30

AKROMID® NEXT S3 GF 30 1 black (8825) is a partially biobased and heat-stabilised PA6.10. With 30% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustai

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID®

UL

NEXT S3 GF 15 1 HU black (8823)

PA6.10 GF 15

AKROMID® NEXT S3 GF 15 1 black (8823) is a partially biobased and heat-stabilised PA6.10. With 15% glass fibre reinforcement, the material is suitable for household and industrial applications with medium demands on strength and stiffness. This susta

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID®

UL

NEXT S3 GF 50 1 HU black (8827)

PA6.10 GF50

AKROMID® NEXT S3 GF 50 1 black (8827) is a partially biobased and heat-stabilised PA6.10. With 50% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength and stiffness. This sustain

Modulus

14.500MPa

Strength

200MPa

Impact

100kJ/m²

AKROMID®

B3 natural (1024)

PA6

AKROMID® B3 natural (1024) is an unreinforced polyamide 6 with light inherent color

Modulus

3.200MPa

Strength

83MPa

Impact

180kJ/m²

AKROMID®

A3 S3 natural (1176)

PA66-I

AKROMID® A3 S3 natural (1176) is an unreinforced, dry impact modified Polyamide 6.6. The material is characterised by a very high impact strength and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and

Modulus

2.800MPa

Strength

67MPa

Impact

180kJ/m²

AKROMID®

B3 3 S3 10 natural (1808)

PA6-I

AKROMID® B3 3 S3 10 natural (1808) is an unreinforced, impact modified Polyamide 6. Furthermore, the material is nucleated. It is suitable for handles and fittings for power tools as well as for the furniture industry. It has a light inherent color.

Modulus

2.700MPa

Strength

70MPa

Impact

180kJ/m²