AKROMID®

Preliminary

B3 GF 30 ECO black (7923)PA6 GF30

AKROMID® B3 GF 30 ECO black (7923) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6. The material is suitable for technical components in mechanical engineering and automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock and thus contribute to reducing the consumption of valuable raw materials.

Features

heat stabilised 130
recycled content
Sports & leisure

Properties

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9500 MPa
5700 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
155 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
75 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
10 kJ/m²
14 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,37 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.