AKROMID®

B3 GF 50 black (4907)

PA6 GF50

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 black (4907) - PA6.6, 50% glass fiber, easy flow, high rigidity and strength

AKROMID®

B28 GF 50 natural (4842)

PA6 GF50

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

Modulus

16.500MPa

Strength

250MPa

Impact

110kJ/m²

AKROMID® B28 GF 50 natural (4842) - 50% glass fibre reinforced, easy flowing, polyamide 6, very high stiffness and strength

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID® A28 GF 50 1 GIT black (5029) - 50% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

AKROMID®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/m²

AKROMID® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMID®

D3 GF 30 1 LT black (5391)

PA612 GF30

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

Modulus

9.200MPa

Strength

170MPa

Impact

85kJ/m²

AKROMID® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

AKROLOY®

PA ICF 30 black (5269)

PA66+PA6I/6T CF30

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

25.000MPa

Strength

220MPa

Impact

50kJ/m²

AKROLOY® PA ICF 30 black (5269) is a 30% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

115161780

AKROMID®

Preliminary

NEXT U28 ICF 40 1 black (8238)PA11 CF40

AKROMID® NEXT U28 ICF 40 1 black (8238) is a Polyamide 11 reinforced with 40% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. The production of large-volume parts is possible with high throughputs > 1 kg/h in 3D-printing with pellets in screw extrusion additive manufacturing and Fused Granulate Fabrication (FGF).

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/m²

Sustainability

Biobased carbon content

41 %

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
20000 MPa
14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
3,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
17500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
295 MPa
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
3,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
80 kJ/m²
75 kJ/m²
75 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
14 kJ/m²
14 kJ/m²
10 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,4 - 0,6 %

Water absorption

ISO 62

23°C, saturated
1,1 - 1,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more