PRECITE®
V GF 20 2 natural (7737)
PBT-ASA- GF 20
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
6.500MPa
110MPa
50kJ/m²
PRECITE V GF 20 2 natural (7737) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.
PRECITE®
E GF 30 LA black (7825)
PET GF 30
PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
10.500MPa
155MPa
45kJ/m²
PRECITE® E GF 30 LA black (7825) ) - PET, 30% glass fibre, high stiffness, high toughness, elevated temperature, good surface, dimensional stability, laser markable, metal replacement, automotive, E&E, household.
AKROMID®
B3 ICF 30 AM black (7451)
PA6 CF30
AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
20.000MPa
190MPa
45kJ/m²
AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
PRECITE®
P3 ICF 15 black (7720)
PBT CF 15
PRECITE® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
12.500MPa
135MPa
50kJ/m²
PRECITE® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.
AKROLOY®
PARA FGF 50 1 black (8186)
PARA FGF50
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
19.000MPa
295MPa
75kJ/m²
AKROLOY® PARA FGF 50 1 black (8186) - polyarylamide, 50% flat glass fiber reinforced, improved properties 90° to the flow direction, easy flowing
AKROMID®
A3 1 S3 natural (2847)
PA66-I
AKROMID® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
2.500MPa
65MPa
180kJ/m²
AKROMID® A3 1 S3 natural (2847) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E
AKROMID®
B3 GF 30 1 L black (4365)
PA6+PP GF30
AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride
8.800MPa
140MPa
60kJ/m²
AKROMID® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROMID®
B28 GF 30 9 FR natural (8069)PA6 GF 30 FR(40)
AKROMID® B28 GF 30 9 FR natural (8069) is a flame retardant PA6 with 30% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed with a V0 classification at 1.6mm. Due to its very good flowability, it is characterised by easy processability as well as good surface properties. The material has excellent long-term thermal stability and outstanding mechanical properties.
Features
Regulatory
Properties
10.200MPa
144MPa
80kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Coefficient of linear thermal expansion
ISO 11359-1/2
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Surface resistivity
DIN EN 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.