PRECITE®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/m²

PRECITE® E ICF 20 black (7428) - PET, 20% recycled carbon fibre , very high stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

PRECITE®

Preliminary

E GF 20 8 black (7849)

PET GF 20 8

PRECITE® E GF 20 8 black (7849) - PET, 20% glass fibre, high stiffness, high toughness, dimensional stability, chemical resistance, food contact, very good surface, kitchen and household appliances.

Modulus

7.800MPa

Strength

NA

Impact

35kJ/m²

PRECITE® E GF 20 8 black (7849) - PET, 20% glass fibre, high stiffness, high toughness, dimensional stability, chemical resistance, food contact, very good surface, kitchen and household appliances.

PRECITE®

Preliminary

P3 ICF 15 black (7720)

PBT CF 15

PRECITE® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

Modulus

12.500MPa

Strength

135MPa

Impact

50kJ/m²

PRECITE® P3 ICF 15 black (7720)- PBT, 15% recycled carbon fibre , medium stiffness and toughness, improved surface finish, good dimensionstability, good tribological properties, reduced density, sustainable, automotive, industrial, E&E, appliance.

AKROMID®

T5 GF 50 black (6247)

PPA GF50

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

AKROMID® T5 GF 50 black (6247) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROLOY®

PA GF 40 black (6416)

PA66+PA6I/6T GF40

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

13.000MPa

Strength

235MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (6416) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

PRECITE®

V GF 30 2 black (7724)

PBT+ASA GF30

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

Modulus

9.500MPa

Strength

130MPa

Impact

60kJ/m²

PRECITE® V GF 30 2 black (7724) - PBT/ASA blend, low warpage, good surface, lower density.

AKROMID®

B3 ICF 30 AM black (7451)

PA6 CF30

AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

Modulus

20.000MPa

Strength

190MPa

Impact

45kJ/m²

AKROMID® B3 ICF 30 AM black (7451) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties as well as optimised viscosity. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.

115161780

AKROMID®

UL

B3 1 black (6528)PA6

AKROMID® B3 1 black (6528) is an unreinforced, heat stabilised polyamide 6

Features

heat stabilised 130

Regulatory

ul

Properties

Modulus

3.600MPa

Strength

85MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3600 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
85 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
20 %
> 50 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
120 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
5 kJ/m²
16 kJ/m²
2 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
60 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 - 140 °C
90 - 120 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class
V-2 Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
4 PLC
3 PLC
3 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
1 PLC
1 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,13 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 3,4 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more