PRECITE®

Preliminary

V GF 20 2 black (7738)

PBT-ASA- GF 20

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

Modulus

6.500MPa

Strength

110MPa

Impact

50kJ/m²

PRECITE V GF 20 2 black (7738) is a 20% glass fibre reinforced, UV-stabilised PBT/ASA blend with low warpage, good surface finish and lower density compared to neat PBT.

AKROMID®

UL

A3 GF 30 FR orange (7871)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

Modulus

10.400MPa

Strength

140MPa

Impact

60kJ/m²

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

PRECITE®

Preliminary

K GF 30 8 natural (7882)

PBT-PET- GF 30

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

Modulus

10.000MPa

Strength

150MPa

Impact

70kJ/m²

PRECITE® K GF 30 8 natural (7882) - PBT/PET blend, 30% glass fibre, high stiffness, low moisture absorption, very good dimensional stability, food contact, very good surface, kitchen and household appliances.

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)

PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

AKROMID® A3 GF 30 6 ECO black (8160) - PA 6.6, 30% glass fiber, recycling, high stiffness and strength, laser-markable, automotive, mechanical engineering.

AKROMID®

Preliminary

B3 GF 50 6 black (20028)

PA6 GF50

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

Modulus

16.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® B3 GF 50 6 black (20028) is a 50% glass fibre reinforced, inorganic high temperature stabilised polyamide 6 with very high stiffness and strength

AKROMID®

B28 GF 30 S3 white (8349)

PA6-I GF30

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

150MPa

Impact

94kJ/m²

AKROMID® B28 GF 30 S3 white (8349) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

AKROMID®

Preliminary

B25 GF 40 L black (8452)

PA6+PP GF40

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

Modulus

11.500MPa

Strength

150MPa

Impact

60kJ/m²

AKROMID® B25 GF 40 L black (8452) is a 40% glass fibre reinforced, very easy flowing polyamide blend with reduced density compared to standard PA6 GF 40.

115161780

AKROLOY®

Preliminary

PA GF 30 black (6415)PA66+PA6I/6T GF30

AKROLOY® PA GF 30 black (6415) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Properties

Modulus

9.800MPa

Strength

200MPa

Impact

65kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9800 MPa
9000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,8 %
2,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9500 MPa
9500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
280 MPa
230 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,4 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
65 kJ/m²
65 kJ/m²
60 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
11 kJ/m²
11 kJ/m²
10 kJ/m²
10 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
235 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
120 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
150 °C
115 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
160 mm
500 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more