PRECITE®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/m²

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROLOY®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROLOY®

Preliminary

PARA GF 35 FR grey (8200)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR grey (8200) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 7035.

AKROTEK®

RA GFM 15/25 black (8216)

PA6 (GF15+MD25)

AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

Modulus

8.500MPa

Strength

120MPa

Impact

50kJ/m²

AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

AKROLOY®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

AKROLOY®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

112131480

AKROMID®

UL

A3 GF 30 FR orange (7871)PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR orange (7871) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors. This material is coloured similar RAL2003

Features

flame retardant

Regulatory

ul

Properties

Modulus

10.400MPa

Strength

140MPa

Impact

60kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
10400 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
60 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
10 kJ/m²
12 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
246 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
261 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
750 °C
750 °C
750 °C
775 °C

HWI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,4 mm Wall thickness
UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC
0 PLC

General properties

Density

ISO 1183

23°C
1,38 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
UL
conditioned
1015 Ω x cm
1013 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1013 Ω
1013 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

UL
3 mm
15 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

High voltage arc tracking rate (HVTR)

UL 746A

UL
1 PLC

High Volt, Low Current Arc Resistance

ASTM D495

UL
6 PLC

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more