AKROMID®

B3 GF 30 2 RM-D black (3424)PA6+ABS GF30

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption. The material is characterised by good adhesion to PUR systems.

Features

UV-stabilised
reduced moisture

Properties

Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9300 MPa
7000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
145 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
210 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
55 kJ/m²
50 kJ/m²
50 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
11 kJ/m²
11 kJ/m²
9 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
175 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,18 10⁻⁴/K
1,05 10⁻⁴/K

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,33 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
12 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical chan

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID®

B3 GF 30 9 RM-M black (3099)

PA6+X GF30

AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/m²

AKROMID®

D3 GF 30 2 black (7026)

PA612 GF30

AKROMID® D3 GF 30 2 black (7026) is a 30% glass fibre reinforced, UV-stabilised polyamide 6.12 with high strength and stiffness. Due to its good chemical resistance, the compound is suitable for media-carrying connectors, which are exposed to UV radi

Modulus

9.500MPa

Strength

180MPa

Impact

95kJ/m²

AKROMID®

B28 GF 30 2 black (7059)

PA6 GF30

AKROMID® B28 GF 30 2 black (7059) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is UV and heat stabilised and therefore perfectly suitable for technical comp

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID®

UL
Preliminary

B28 GF 25 9 FR black (8250)

PA6 GF25 FR(44)

AKROMID® B28 GF 25 9 FR black (8250) is a flame retardant PA6 with 25% glass fibres and a better UV-stability than the standard AKROMID® B28 GF 25 9 FR black (8253). The flame retardant system is free of red phosphorus and halogens, leading to optimi

Modulus

9.000MPa

Strength

135MPa

Impact

81kJ/m²

AKROMID®

B28 GF 30 6 LT black (8500)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (8500) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is UV- and high heat stabilised and therefore perfectly suitable for automot

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID®

NEXT B28 GF 30 2 black (7059BMBCI)

PA6 GF30

AKROMID®NEXT B28 GF 30 2 black (7059BMBCI) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is UV and heat stabilised and therefore perfectly suitable for techn

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID®

Preliminary

NEXT B3 GF 30 1 L black (5212BMBCI)

PA6+PP GF30

AKROMID® NEXT B3 GF 30 1 L black (5212BMBCI) is a PA6/PP-blend with reduced density compared to standard PA6 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where weight reduction ar

Modulus

9.000MPa

Strength

135MPa

Impact

58kJ/m²

AKROMID®

B3 GF 30 S1 black (2091)

PA6-I GF30

AKROMID® B3 GF 30 S1 black (2091) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfec

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 25 1 black (2484)

PA6 GF25

PLACEHOLDER

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 black (2493)

PA6 GF30

PLACEHOLDER

Modulus

10.300MPa

Strength

185MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 1 black (2485)

PA6 GF30

AKROMID® B3 GF 30 1 black (2485) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engine

Modulus

10.300MPa

Strength

175MPa

Impact

80kJ/m²