Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROLOYĀ®

UL

PARA GF 40 HU natural (8512)

PARA GF40

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

15.000MPa

Strength

255MPa

Impact

NA

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/mĀ²

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

AKROLOYĀ®

Preliminary

PA CF 40 1 black (8504)

PA66+PA6I/6T CF40

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

Modulus

33.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR natural (8744)

PK GF 10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

AKROLOYĀ®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

PRECITEĀ®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/mĀ²

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMIDĀ®

C28 GF 25 FRT natural (7332)

PA-Blend

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/mĀ²

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

112131480

AKROMIDĀ®

Preliminary

T9 GF 50 black (7601)PPA GF50

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Features

heat stabilised 160

Properties

Modulus

17.000MPa

Strength

250MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
250 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
95 kJ/mĀ²
80 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
16 kJ/mĀ²
14 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
305 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,55 g/cmĀ³

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.