HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITEĀ®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/mĀ²

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROLOYĀ®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROLOYĀ®

Preliminary

PA CF 40 1 black (8504)

PA66+PA6I/6T CF40

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

Modulus

33.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

AKROMIDĀ®

Preliminary

B3 GF 40 S1 black (8647)

PA6-I GF40

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/mĀ²

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

UL

PARA GF 40 HU natural (8512)

PARA GF40

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

15.000MPa

Strength

255MPa

Impact

NA

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR natural (8744)

PK GF 10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

AKROMIDĀ®

B3 GFM 15/25 black (1312)

PA6 (GF15+MD25)

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/mĀ²

AKROMIDĀ® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

112131480

PRECITEĀ®

Preliminary

E GF 40 natural (7304)PET GF 40

PRECITEĀ® E GF 40 natural (7304) is a 40% glass fibre reinforced, medium viscous polyethylene terephthalate (PET) with high stiffness and toughness even at elevated temperatures. Due to its low moisture absorption, this material is particularly dimensionally stable and therefore perfectly suitable for precision parts in the automotive, E&E and household goods industries, where a very good surface finish is required.

Features

surface modified
reduced moisture
E&E
metal substitution
Sports & leisure

Properties

Modulus

15.000MPa

Strength

195MPa

Impact

64kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
195 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
1,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
15500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
300 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
64 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
233 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
250 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,65 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.