HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROLOYĀ®

UL

PARA GF 40 HU natural (8512)

PARA GF40

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

15.000MPa

Strength

255MPa

Impact

NA

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/mĀ²

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

AKROLOYĀ®

Preliminary

PA CF 40 1 black (8504)

PA66+PA6I/6T CF40

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

Modulus

33.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR natural (8744)

PK GF 10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

AKROLOYĀ®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

PRECITEĀ®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/mĀ²

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMIDĀ®

C28 GF 25 FRT natural (7332)

PA-Blend

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/mĀ²

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

112131480

PRECITEĀ®

P3 GF 30 natural (6850)PBT GF30

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Properties

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
11 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

General properties

Density

ISO 1183

23Ā°C
1,53 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23Ā°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
> 1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
350 V

Rheological Properties

MVR

ISO 1133

250Ā°C/2,16kg
9 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more