AKROLOY®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

PRECITE®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/m²

PRECITE®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROLOY®

UL

PARA GF 40 HU natural (8512)

PARA GF40

AKROLOY® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

15.000MPa

Strength

255MPa

Impact

NA

AKROLOY® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMID®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/m²

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

AKROLOY®

Preliminary

PA CF 40 1 black (8504)

PA66+PA6I/6T CF40

AKROLOY® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

Modulus

33.000MPa

Strength

310MPa

Impact

80kJ/m²

AKROLOY® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

AKROTEK®

Preliminary

PK-VM GF 10 FR natural (8744)

PK GF 10 FR(40)

AKROTEK® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/m²

AKROTEK® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

AKROMID®

B3 GF 30 S1 natural (1383)

PA6-I GF30

AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

112131480

AKROMID®

B3 ICF 15 black (5026)PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a 15% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties.

Properties

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²

Sustainability

Recycled content

15 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
5000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
140 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
9000 MPa
7000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
150 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,5 %
6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
55 kJ/m²
80 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
6 kJ/m²
10 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,17 10⁻⁴/K
0,66 10⁻⁴/K

Thermal conductivity

DIN 52612

0,31 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,19 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
105 Ω
105 Ω

Rheological Properties

Flowability

AKRO

2 mm Thickness
360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more