AKROLOYĀ®

UL

PARA GF 40 HU natural (8512)

PARA GF40

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

15.000MPa

Strength

255MPa

Impact

NA

AKROLOYĀ® PARA GF 40 HU natural (8512) - PARA, 40% GF, high modulus and strength, easy flowing, listed at UL in all colors, metal substitute

AKROMIDĀ®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/mĀ²

AKROMIDĀ® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

AKROLOYĀ®

Preliminary

PA CF 40 1 black (8504)

PA66+PA6I/6T CF40

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

Modulus

33.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications

AKROTEKĀ®

Preliminary

PK-VM GF 10 FR natural (8744)

PK GF 10 FR(40)

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

Modulus

4.000MPa

Strength

70MPa

Impact

48kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 FR natural (8744) - Polyketon, 10% GF, chemical and hydrolysis resistance, flame retardant, halogen free, process improved, good dimensional stability, high voltage components, e-mobility.

AKROLOYĀ®

UL

PARA GF 50 HU natural (8595)

PARA GF50

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

Modulus

19.000MPa

Strength

310MPa

Impact

80kJ/mĀ²

AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute

PRECITEĀ®

Preliminary

E GF 30 4 black (8622)

PET-I GF30

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.400MPa

Strength

135MPa

Impact

70kJ/mĀ²

PRECITEĀ®E GF 30 4 black (8622) - PET, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMIDĀ®

C28 GF 25 FRT natural (7332)

PA-Blend

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/mĀ²

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

112131480

AKROMIDĀ®

A3 GF 35 3 black (1802)PA66 GF35

AKROMIDĀ® A3 GF 35 3 black (1802) is a 35% glass fiber reinforced polyamide 6.6. It is characterised by a high stiffness and strength. Furthermore, the material is nucleated. It is perfectly suitable for technical parts in industrial engineering and in the automotive industry.

Features

nucleated

Properties

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11500 MPa
8400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
180 MPa
120 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,3 %
4,2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
> 55 kJ/mĀ²
53 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
9 kJ/mĀ²
13 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
265 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,65 - 0,85 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more