AKROMID®

Preliminary

B3 GF 33 natural (2863)PA6 GF33

AKROMID B3 GF 33 natural (2863) is a 33% glass fiber reinforced polyamide 6 with high rigidity and strength

Properties

Modulus

11.000MPa

Strength

190MPa

Impact

80kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
11000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,37 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend GF25 FR(44)

C28 GF 25 FRT natural (7332) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

AKROMID®

B3 GF 30 S1 natural (1383)

PA6-I GF30

AKROMID® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perf

Modulus

8.000MPa

Strength

125MPa

Impact

110kJ/m²

AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 25 natural (2471)

PA6 GF25

AKROMID® B3 GF 25 natural (2471) is a 25% glass fibre reinforced polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID®

B3 GF 30 RM-M natural (3291)

PA6+X GF30

AKROMID® B3 GF 30 RM-M natural (3291) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical ch

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID®

Preliminary

B3 GF 25 1 L natural (4781)

PA6+PP GF25

AKROMID® B3 GF 25 1 L natural (4781) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are requ

Modulus

7.200MPa

Strength

130MPa

Impact

70kJ/m²

AKROMID®

B28 GF 30 natural (4826)

PA6 GF30

AKROMID® B28 GF 30 natural (4826) is a 30% glass fiber reinforced, easy flowing polyamide 6. It is characterised by a high stiffness and strength. The material is therefore perfectly suitable for technical parts not only in industrial engineering and

Modulus

9.500MPa

Strength

180MPa

Impact

90kJ/m²

AKROMID®

B28 GF 30 9 natural (6614)

PA6 GF30

AKROMID® B28 GF 30 9 natural (6614) is a 30% glass fibre reinforced, easy flowing polyamide 6. The material is characterised by good surface properties due to its very good flowability. Furthermore, the material is easy to color. Owing to its high st

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID®

Preliminary

B28 GF 30 natural (6941)

PA6 GF30

AKROMID B28 GF 30 natural (6941) is a 30% glass fibre reinforced, easy flowing PA6. Due to its very good flowability, this grade has a good surface. It complies with the bus fire standard ECE R 118.03 annex 6 and 8 and is suitable for panels, seat sh

Modulus

10.200MPa

Strength

180MPa

Impact

80kJ/m²

AKROMID®

UL
Preliminary

B28 GF 25 9 FR natural (8066)

PA6 GF25 FR(44)

AKROMID® B28 GF 25 9 FR natural (8066) is a flame retardant PA6 with 25% glass fibres. The flame retardant system is free of red phosphorus and halogens, leading to optimised electrical properties for e-mobility applications. This grade is UL listed

Modulus

8.900MPa

Strength

138MPa

Impact

83kJ/m²

AKROMID®

B3 GF 30 AM natural (8962)

PA6 GF30

AKROMID® B3 GF 30 AM natural (8962) is a 30% glass fiber reinforced polyamide 6 with high stiffness and good sliding properties as well as optimized viscosity. It is suitable for pellet-based large format additive manufacturing processes (LFAM, FGF)

Modulus

8.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID®

UL
Preliminary

B25 GF 30 1 FR natural (8954)

PA6 GF30 FR(44)

AKROMID® B25 GF 30 1 FR natural (8954) is an UL-listed, flame-retardant, heat-stabilised and 30% glass fibre-reinforced PA6. The material is based on a flame-retardant system that is free of red phosphorus, halogens, melamine, zink borate and PFAS. I

Modulus

11.000MPa

Strength

145MPa

Impact

65kJ/m²