AKROTEK®

PK-VM GF 30 black (8655)

PK GF30

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.500MPa

Strength

130MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 black (8655) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROMID®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/m²

AKROMID® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMID®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/m²

AKROMID® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMID®

UL

C3 GF 30 1 FR black (7243)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL
Preliminary

C3 GF 30 1 FR natural (7207)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.500MPa

Strength

150MPa

Impact

76kJ/m²

AKROMID® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL

C3 GF 30 1 FR white (7630)

PA6+PA66 GF30 FR(40)

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

140MPa

Impact

NA

AKROMID® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

AKROMID®

Preliminary

T5 GF 50 6 natural (8056)

PPA GF50

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 natural (8056) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps its mechanical performance even at elevated temperatures or moisture pick-up

Modulus

18.000MPa

Strength

270MPa

Impact

90kJ/m²

Standard Grade with good surface quality. AKROMID® T5 GF 50 6 natural (8056) is a 50% glass fibre reinforced polyphthalamide with anorganic heat stabilization, very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps its mechanical performance even at elevated temperatures or moisture pick-up

123480

AKROLOY®

PA ICF 20 black (5268)PA66 + PA6I/6T CF20

AKROLOY® PA ICF 20 black (5268) is a 20% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Properties

Modulus

17.000MPa

Strength

200MPa

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
17000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
200 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
13000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
45 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
6 kJ/m²
5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
223 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 %
0,6 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
105 Ω

Rheological Properties

Flowability

AKRO

2 mm Thickness
440 mm

MVR

ISO 1133

275°C/5kg
40 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more