HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

PRECITE®

Preliminary

K GF 30 4 LA ECO black (8699)

PBT-PET- GF 30

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

Modulus

9.500MPa

Strength

120MPa

Impact

65kJ/m²

PRECITE® K GF 30 4 ECO black (8699) - PBT/PET blend, regenerated post-consumer PET, glass fibre, hydrolysis stabillised, high strength, good dimensional stability, automotive, industrial, household, E&E, sports & leisure.

AKROMID®

Preliminary

A3 1 S3 black (11392)

PA66-I

AKROMID® A3 1 S3 black (11392) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, low emission

Modulus

2.300MPa

Strength

60MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 black (11392) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, low emission

AKROMID®

UL

C3 GF 30 1 FR black (7243)

PA66+PA6 GF30 FR(40)

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.800MPa

Strength

148MPa

Impact

74kJ/m²

AKROMID® C3 GF 30 1 FR black (7243) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

AKROMID®

UL
Preliminary

B28 GF 35 9 FR orange (8573)

PA6 GF35 FR(40)

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

Modulus

12.600MPa

Strength

145MPa

Impact

60kJ/m²

AKROMID® B28 GF 35 9 FR orange (8573) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL listed V0 from 1,6 mm, RAL 2003, e-mobility.

PRECITE®

Preliminary

P3 GF 30 4 LA black (8286)

PBT-I GF30

PRECITE®P3 GF 30 4 LA black (8286) PBT, 30% GF, hydrolysis stabilised, laser markable high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability, light black

Modulus

9.100MPa

Strength

120MPa

Impact

70kJ/m²

PRECITE®P3 GF 30 4 LA black (8286) PBT, 30% GF, hydrolysis stabilised, laser markable high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability, light black

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR black (8604)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR black (8604) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility, lasermarkable.

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR black (8604) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility, lasermarkable.

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR natural (8448)

PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR natural (8448) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility.

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

AKROTEK® PK-VM GF 30 FR natural (8448) - Polyketon, 30% GF, chemical and hydrolysis resistance, flame retardant, halogenefree, process improved, good dimensional stability. high voltage components, e-mobility.

123480

AKROMID®

A3 5 black (4701)PA66

AKROMID® A3 5 black (4701) is an unreinforced, high temperature stabilised polyamide 6.6

Features

heat stabilised 160

Properties

Modulus

3.500MPa

Strength

90MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
3500 MPa
1450 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
90 MPa
55 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
12 %
≥ 30 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
125 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
≥ 4,5 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-2 Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,14 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more