PK-VM GF 15 black (8686)

PK GF15

AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

4.500MPa

Strength

90MPa

Impact

50kJ/mĀ²

AKROTEKĀ® PK-VM GF 15 black (8686) - Polyketon, 15% glass fibre reinforced, chemical and hydrolysis resistance

AKROMIDĀ®

UL

C3 GF 25 1 FR natural (7208)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.200MPa

Strength

140MPa

Impact

73kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR natural (7208) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMIDĀ®

UL

C3 GF 25 1 FR black (7246)

PA66+PA6 GF25 FR(40)

AKROMIDĀ® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

Modulus

9.100MPa

Strength

137MPa

Impact

66kJ/mĀ²

AKROMIDĀ® C3 GF 25 1 FR black (7246) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, high strength, UL-listed, automotive, E&E market.

AKROMIDĀ®

UL

C3 GF 30 1 FR white (7630)

PA6+PA66 GF30 FR(40)

AKROMIDĀ® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

Modulus

10.600MPa

Strength

140MPa

Impact

NA

AKROMIDĀ® C3 GF 30 1 FR white (7630) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 9016, E&E, Public transportation EN 45545-2.

AKROLOYĀ®

UL

PA GF 50 HU black (8198)

PA66+PA6I/6T GF50

AKROLOYĀ® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

265MPa

Impact

105kJ/mĀ²

AKROLOYĀ® PA GF 50 HU black (8198) is an UL listed, 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROMIDĀ®

UL
Preliminary

C3 GF 30 1 FR grey (8384)

PA66+PA6 GF30 FR(40)

AKROMIDĀ® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

Modulus

10.000MPa

Strength

121MPa

Impact

46kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 FR grey (8384) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, RAL 7035, E&E, Public transportation EN 45545-2.

AKROMIDĀ®

UL
Preliminary

C3 GF 30 1 FR natural (7207)

PA66+PA6 GF30 FR(40)

AKROMIDĀ® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

Modulus

10.500MPa

Strength

150MPa

Impact

76kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 FR natural (7207) - PA6/6.6 blend, 30 % glass fiber, flame retardant, good flowability, UL-listed, E&E, Public transportation EN 45545-2.

123480

AKROMIDĀ®

B3 GF 25 1 L black (4637)PA6+PP GF25

AKROMIDĀ® B3 GF 25 1 L black (4637) is a PA6/PP-blend with reduced density compared to standard PA6 with 25% glass fibre reinforcement. The material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 25 1 L black (4637) is particularly superior to calcium chloride (CaClā‚‚).

Features

heat stabilised 130
reduced density

Properties

Modulus

7.500MPa

Strength

135MPa

Impact

68kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
5600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
135 MPa
88 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,3 %
4,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
68 kJ/mĀ²
58 kJ/mĀ²
67 kJ/mĀ²
54 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
15 kJ/mĀ²
15 kJ/mĀ²
13 kJ/mĀ²
10 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
198 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
217 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
750 Ā°C
725 Ā°C
750 Ā°C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
775 Ā°C
750 Ā°C
775 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,22 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,55 - 0,75 %

Rheological Properties

MVR

ISO 1133

275Ā°C/5kg
10 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more