AKROMID®
B3 ICF 40 AM black (8236)
PA6 CF40
AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
27.000MPa
210MPa
45kJ/m²
AKROMID® B3 ICF 40 AM black (8236) is a 40% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties. It is suitable for a stable additive manufacturing process (3D Printing) at fast production speeds.
AKROMID®
NEXT B3 GF 30 1 L CR black (8313)
PA6 + PP GF30
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
8.800MPa
140MPa
70kJ/m²
AKROMID® NEXT B3 GF 30 1 L CR black (8313) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.
AKROMID®
NEXT S3 GF 30 S1 black (8887)
PA610-I GF30
AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.
7.800MPa
135MPa
100kJ/m²
AKROMID® NEXT S3 GF 30 S1 black (8887) - PA6.10 partly bio-based, sustainable, low moisture absorption, high strength and stiffness, high chemical resistance, impact modified, household, industrial application.
AKROMID®
B3 GF 30 S1 natural (1383)
PA6-I GF30
AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
7.500MPa
125MPa
110kJ/m²
AKROMID® B3 GF 30 S1 natural (1383) - PA 6, 30% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive
AKROMID®
B3 GFM 15/25 black (1312)
PA6 (GF15+MD25)
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
8.000MPa
120MPa
50kJ/m²
AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability
AKROMID®
C28 GF 25 FRT natural (7332)
PA-Blend
C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.
10.800MPa
157MPa
64kJ/m²
C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.
AKROMID®
B3 GK 30 black (1827)
PA6 GB30
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
4.500MPa
75MPa
20kJ/m²
AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage
PRECITE®
P3 GF 30 9 FR black (8424)PBT GF30 FR(40)
PRECITE® P3 GF 30 9 FR black (8424) is a 30% glass fibre reinforced, flame retardant polybutylene terephthalate (PBT) with high stiffness and strength. The material offers outstanding long-term heat-aging stability as well as mechanical advantages to conventional products. It achieves V0 classification at thicknesses of 1.6 mm and above by using a flame retardant system which is free of red phosphorous and halogens. Due to its low moisture absorption, this material has very good dimensional stability and it is particularly suitable for precision parts in E-Mobility or E&E industry.
Features
Properties
10.500MPa
122MPa
50kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
Burning rate (<100 mm/min)
FMVSS 302
Oxygen index
ISO 4589-2
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.