AKROMID®

B3 GF 15 8 L natural (5689)PA6+PP GF15

AKROMID® B3 GF 15 8 L natural (5689) is a PA6/PP-blend with reduced density compared to standard PA6 with 15% glass fibre reinforcement. The material is suitable for components with average strength and stiffness where cost and weight reduction are required at the same time. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.

Features

reduced density

Regulatory

eu102011fda

Properties

Modulus

5.200MPa

Strength

110MPa

Impact

65kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
12 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
190 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,14 g/cm³

Rheological Properties


MVR

ISO 1133

275°C/5kg
25 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.