AKROLEN®

Preliminary

PP LGF 40 2 black (8488)PP LGF40

AKROLEN® PP LGF 40 2 black (8488) is a polypropylene copolymer with 40% long glass fibre reinforcement which leads to a very high stiffness and strength. The materials very good surface quality as well as the outstanding UV-stability make it the product of your choice for technical parts which are exposed to UV radiation. This type is also available with biomass-balanced PP copo to reduce the CO2 footprint = AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI).

Features

UV-stabilised
Sports & leisure

Properties

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
81 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
32 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
165 °C

General properties


Density

ISO 1183

23°C
1,23 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.