PRECITE®

Preliminary

P3 GF 30 9 FR black (8424)PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR black (8424) is a 30% glass fiber-reinforced, flame-retardant polybutylene terephthalate (PBT) with a very good combination of strength and ductility and a UL94 V-0 classification from 1.6 mm thickness. The material is based on the latest flame retardant technology and is free from halogenated flame retardant additives, antimony trioxide, PFAS and melamine containing components. It offers excellent heat ageing resistance and is very dimensionally stable due to its low moisture absorption and is particularly suitable for precision parts in the e-mobility or E&E industry.

Features

heat stabilised 130
flame retardant
low warpage
E&E
E-Mobility

Properties

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
122 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
197 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
50 kJ/m²
58 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
222 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
224 °C

Flammability

Flammability

UL 94

1,6 mm Wall thickness
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
750 °C
750 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 30 %

General Properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,8 - 1,0 %

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
25,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.