B3 GF 50 1 black (2488)

PA6 GF50

AKROMIDĀ® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

17.000MPa

Strength

230MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 50 1 black (2488) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 GF 30 1 L black (4365)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

8.800MPa

Strength

140MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L black (4365) - PA6/PP-Blend glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

B3 GF 60 4 RM-M natural (4645)

PA6 + X GF60

AKROMIDĀ® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

Modulus

21.500MPa

Strength

235MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 60 4 RM-M natural (4645) is a 60% glass fiber reinforced, hydrolysis- and chemical stabilised polyamide 6 with low humidity absorption, very good surface finish and light inherent color.

AKROMIDĀ®

B3 GF 60 4 RM-M black (5238)

PA6+X GF60

AKROMIDĀ® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

Modulus

22.500MPa

Strength

225MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 60 4 RM-M black (5238) is a 60% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish.

AKROMIDĀ®

B3 GF 15 1 L black (4670)

PA6+PP GF15

AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

105MPa

Impact

60kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 L black (4670) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

D3 GF 30 1 LT black (5391)

PA612 GF30

AKROMIDĀ® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

Modulus

9.200MPa

Strength

170MPa

Impact

85kJ/mĀ²

AKROMIDĀ® D3 GF 30 1 LT black (5391) - PA 6.12, glass fiber, laser-transparent,connector

AKROMIDĀ®

B3 GF 30 1 EN black (5637)

PA6 GF30

AKROMIDĀ® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 EN black (5637) - 30% glass fiber reinforced PA 6, electrically neutral, heat stabilised, technical parts in industrial engineering and automotive industry

114151680

AKROMIDĀ®

A3 ICF 20 black (5102)PA66 CF20

AKROMIDĀ® A3 ICF 20 black (5102) is a 20% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

16.000MPa

Strength

190MPa

Impact

50kJ/mĀ²

Sustainability

Recycled content

20 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
16000 MPa
9500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
14000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
280 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
50 kJ/mĀ²
60 kJ/mĀ²
40 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
6 kJ/mĀ²
8 kJ/mĀ²
4 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
250 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,10 10ā»ā“/K
0,90 10ā»ā“/K

Thermal conductivity

DIN 52612

0,34 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,23 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,2 - 2,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,6 - 0,8 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
104 ā„¦
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more