Description

AKROMID®

B3 GFM 15/25 black (1312)

PA6 (GF15+MD25)

AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

AKROMID® B3 GFM 15/25 black (1312) is a 15% glass fibre reinforced, 25% mineral filled polyamide 6 with good surface and dimensional stability

AKROMID®

C28 GF 25 FRT natural (7332)

PA-Blend

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

Modulus

10.800MPa

Strength

157MPa

Impact

64kJ/m²

C28 GF 25 FRT natural (7332) - PA blend, 25% glass fiber, flame retardant, good flowability, Public Transportation EN 45545-2.

AKROMID®

B3 GK 30 black (1827)

PA6 GB30

AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.500MPa

Strength

75MPa

Impact

20kJ/m²

AKROMID® B3 GK 30 black (1827) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

A3 GF 40 1 black (2386)

PA66 GF40

AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 black (2386) - 40% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 30 1 natural (2391)

PA66 GF30

AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 1 natural (2391) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMID®

A3 GF 30 1 black (2385)

PA66 GF30

AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 1 black (2385) - PA 6.6 30% glass fiber reinforced, heat stabilised, technical parts in industrial engineering and in the automotive industry

AKROMID®

B3 GF 30 natural (2472)

PA6 GF30

AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® B3 GF 30 natural (2472) - 30% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

113141580

AKROMID®

Preliminary
Internal

T9 GF 15 FR LA black (8197)PPA GF15 FR(40)

AKROMID® T9 GF 15 FR LA black (8197) is a flame retardant, 15% glass fibre reinforced polyphthalamide. The product is based on PA9T and has a significantly lower moisture absorption compared to conventional PA6T grades. As a result, the glass transition area is much more constant and even in the conditioned state, the product impresses with its medium strength and stiffness. Due to its high temperature and media resistance, this material is suitable for technical components that come into contact with chemicals. The flame retardant system is free of red phosphorus and halogens. This type is laser-markable.

Features

flame retardant
laser markable

Properties

Modulus

6.000MPa

Strength

107MPa

Impact

48kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
6000 MPa
6000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
107 MPa
101 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,2 %
2,8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
48 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
6 kJ/m²
6 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
305 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
960 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0.2 - 0.4 %
0.6 - 0.8 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1014 Ω x cm
1014 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1013 Ω
1012 Ω

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more