AKROMIDĀ®

Preliminary

B28 GF 30 natural (4826)

PA6 GF30

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

Modulus

9.500MPa

Strength

180MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B28 GF 30 S3 natural (8348)

PA6-I GF30

AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

160MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

AKROMIDĀ®

B3 GF 40 black (6077)

PA6 GF40

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

PRECITEĀ®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROLOYĀ®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROMIDĀ®

Preliminary

B3 GF 40 S1 black (8647)

PA6-I GF40

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/mĀ²

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

111121380

AKROMIDĀ®

A28 LGF 50 9 black (7705)PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) is an easy flowing PA6.6 with 50% long glass fibre reinforcement which leads to an extraordinary high stiffness and strength even at high temperature. The material distinguishes itself due to its isotropic mechanical properties as well as increased creep resistance and higher heat deflection temperature. The excellent fatigue performance, high energy absorption in the event of a crash and low shrinkage make it the product of your choice for technical parts e.g. oil pan.

Features

easy flow
process improved

Properties

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
14200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
2,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
45 kJ/mĀ²
45 kJ/mĀ²

Izod impact strength

ISO 180/1A

23Ā°C | d.a.m.
90 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
60 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,25 10ā»ā“/K
0,75 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.