AKROMID®

A3 2 S1 white (5973)PA66-I

AKROMID® A3 2 S1 white (5973) is an unreinforced, impact modified PA 6.6. The material is UV-stabilised and characterised by a very high cold impact strength. Therefore, it is perfectly suitable for connecting and fixing systems which are used in the automotive, electro and furniture industry where a very high impact strength even at low temperatures is required. The color is similar to RAL 9010.

Features

UV-stabilised
impact modified

Properties

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1700 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
45 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
≥ 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
> 80 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
80 MPa

Thermal Properties


Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,07 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.