AKROMID®

A3 GF 15 1 GIT black (4620)PA66 GF15

AKROMID® A3 GF 15 1 GIT black (4620) is a 15% glass fibre reinforced, heat stabilised, easy flowing polyamide 6.6. It is characterised by average stiffness and strength and shows an excellent surface. Furthermore, the material is designed for gas injection technology.

Features

heat stabilised 130
surface modified
fluid injection (GIT/WIT/FIT)

Properties

Modulus

5.500MPa

Strength

125MPa

Impact

40kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
5500 MPa
3500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
80 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
12 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
40 kJ/m²
75 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
7 kJ/m²
8 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,9 - 1,1 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

A28 GF 50 1 GIT black (5029)

PA66 GF50

AKROMID® A28 GF 50 1 GIT black (5029) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6.6. It is characterised by very high stiffness and strength and shows an excellent surface. Furthermore, the material is designed for gas

Modulus

17.500MPa

Strength

270MPa

Impact

100kJ/m²

AKROMID®

UL

A3 GF 50 9 HU black (6500)

PA66 GF50

AKROMID® A3 GF 50 9 HU black (6500) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6.6. It is characterised by very high stiffness and strength and shows an excellent surface. Furthermore, the material is designed for gas in

Modulus

16.500MPa

Strength

265MPa

Impact

NA

AKROMID®

A3 GF 20 1 black (2307)

PA66 GF20

AKROMID® A3 GF 20 1 black (2307) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID®

A3 GF 15 1 black (2382)

PA66 GF15

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

6.400MPa

Strength

130MPa

Impact

35kJ/m²

AKROMID®

B3 GF 30 1 GIT black (4598)

PA6 GF30

AKROMID® B3 GF 30 1 GIT black (4598) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding.

Modulus

9.500MPa

Strength

175MPa

Impact

NA

AKROMID®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMID® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/m²

AKROMID®

B28 GF 33 1 GIT black (6846)

PA6 GF33

AKROMID® B28 GF 33 1 GIT black (6846) is a 33% glass fiber reinforced, heat-stabilized polyamide 6. It is characterized by high rigidity and strength. The material also impresses with its very good processability using the internal gas pressure proce

Modulus

10.500MPa

Strength

190MPa

Impact

95kJ/m²

AKROMID®

B3 GF 30 1 GIT LA black (8278)

PA6 GF30

AKROMID® B3 GF 30 1 GIT LA black (8278) is a 30% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength for gas injection technology and suitable for IR welding. The material is lasermarkable.

Modulus

9.300MPa

Strength

175MPa

Impact

NA

AKROMID®

Preliminary

A3 GF 25 9 FR black (7957)

PA66 GF25 FR(44)

AKROMID® A3 GF 25 9 FR black (7957) is a 25 % glass fibre reinforced, flame-retardant and heat-stabilized PA6.6, coloured in black similar to RAL 9005. The material is based on a flame retardant system that is free of red phosphorus, halogens, antim

Modulus

9.000MPa

Strength

140MPa

Impact

65kJ/m²

AKROMID®

Preliminary

A3 GF 30 7 FR black (8820)

PA66 GF30 FR(44)

AKROMID® A3 GF 30 7 FR black (8820) is a 30 % glass fibre reinforced, flame-retardant and heat-stabilized PA6.6, coloured in black similar to RAL 9005. The material is based on a flame retardant system that is free of red phosphorus, halogens, antimo

Modulus

10.500MPa

Strength

150MPa

Impact

65kJ/m²

AKROMID®

A3 GF 20 1 natural (1261)

PA66 GF20

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID®

A3 GF 40 1 black (2386)

PA66 GF40

AKROMID® A3 GF 40 1 black (2386) is a 40% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²