AKROMIDĀ®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/mĀ²
AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOYĀ®
PA GF 60 black (6418)
PA66+PA6I/6T GF60
AKROLOYĀ® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
21.000MPa
275MPa
100kJ/mĀ²
AKROLOYĀ® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMIDĀ®
T5 GF 35 4 black (7692)
PPA GF35
AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
13.500MPa
220MPa
70kJ/mĀ²
AKROMIDĀ® T5 GF 35 4 black (7692) is a 35% glass fibre reinforced polyphthalamide with inorganic heat stabilization, very high rigidity and strength, designed for hydrolysis resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up
AKROTEKĀ®
RA GFM 15/25 black (8216)
PA6 (GF15+MD25)
AKROTEKĀ® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz
8.500MPa
120MPa
50kJ/mĀ²
AKROTEKĀ® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz
AKROMIDĀ®
A3 GF 30 8 HU black (8112)
PA66 GF30
AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMIDĀ®
B28 GF 30 S3 natural (8348)
PA6-I GF30
AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
8.900MPa
160MPa
100kJ/mĀ²
AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
AKROLOYĀ®
PA CF 40 1 black (8504)
PA66+PA6I/6T CF40
AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications
33.000MPa
310MPa
80kJ/mĀ²
AKROLOYĀ® PA CF 40 1 black (8504) - semi-aromatic polyamide blend, 40% carbon fiber reinforced, perfectly suitable for sport & leisure applications
AKROMIDĀ®
B3 GF 40 1 L black (4581)PA6 + PP GF40
AKROMIDĀ® B3 GF 40 1 L black (4581) is a PA6/PP-blend with reduced density compared to standard PA6 with 40% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® B3 GF 40 1 L black (4581) is particularly superior to calcium chloride (CaClā).
Features
Properties
11.000MPa
150MPa
70kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.