AKROLOY®

PA GF 50 natural (6414)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

275MPa

Impact

110kJ/m²

AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

PA GF 60 black (6418)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

AKROLOY® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROMID®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

D3 GF 30 1 black (5392)

PA612 GF30

AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

Modulus

9.500MPa

Strength

180MPa

Impact

95kJ/m²

AKROMID® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector

AKROMID®

B28 GF 30 S3 natural (8348)

PA6-I GF30

AKROMID® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

160MPa

Impact

100kJ/m²

AKROMID® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

111121380

AKROMID®

B3 GK 30 natural (2719)PA6 GB30

AKROMID® B3 GK 30 natural (2719) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

surface modified
low warpage

Properties

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4400 MPa
1820 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
70 MPa
38 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
35 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3140 MPa
1570 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
95 MPa
55 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
3 kJ/m²
5 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | conditioned
961N/30s | d.a.m.
90 MPa
180 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Vicat softening temperature B50

ISO 306

50°C/50N
205 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,34 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Water absorption

ISO 62

23°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,9 %
1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Rheological Properties

MVR

ISO 1133

275°C/5kg
100 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more