Select your fitting and find the right compound for your intend
AKROMIDĀ®
B3 GF 30 FR natural (7458)
PA6 GF30 FR(40)
AKROMIDĀ® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.
10.800MPa
135MPa
65kJ/mĀ²
AKROMIDĀ® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.
AKROMIDĀ®
A3 GM 20/10 4 WIT black (4529)
PA66 (GF20+GB10)
AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
8.200MPa
175MPa
65kJ/mĀ²
AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage
AKROMIDĀ®
D3 GF 30 1 black (5392)
PA612 GF30
AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
9.500MPa
180MPa
95kJ/mĀ²
AKROMIDĀ® D3 GF 30 1 black (5392) - PA 6.12, 30% glass fiber, connector
AKROMIDĀ®
T9 GF 50 black (7601)
PPA GF50
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
B28 GF 60 1 natural (4775)
PA6 GF60
AKROMIDĀ® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
22.000MPa
260MPa
100kJ/mĀ²
AKROMIDĀ® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
AKROMIDĀ®
B28 GF 30 S3 natural (8348)
PA6-I GF30
AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
8.900MPa
160MPa
100kJ/mĀ²
AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry
AKROLOYĀ®
PARA GF 50 HU natural (8595)
PARA GF50
AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
19.000MPa
310MPa
80kJ/mĀ²
AKROLOYĀ® PARA GF 50 HU natural (8595) - PARA, 50% GF, highed modulus and strength, easy flowing, listed at UL in all colors, metal substitute
AKROMIDĀ®
AKROMIDĀ® A3 GF 35 2 black (21010) is a 35% glass fibre reinforced, UV-stabilised polyamide 6.6 with high stiffness and strength
Features
Properties
12.000MPa
185MPa
50kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN 62631-3-2
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.