AKROMIDĀ®

Preliminary

B28 GF 30 natural (4826)

PA6 GF30

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

Modulus

9.500MPa

Strength

180MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B28 GF 30 natural (4826) - 30% glass fiber reinforced PA 6, easy flowing, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B28 GF 30 S3 natural (8348)

PA6-I GF30

AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

Modulus

8.900MPa

Strength

160MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 GF 30 S3 natural (8348) - PA6, 30% glass fibre reinforced, easy flowing and impact modified, for applications in the furniture industry

AKROMIDĀ®

B3 GF 40 black (6077)

PA6 GF40

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROLOYĀ®

Preliminary

PARA GF 35 FR orange (8039)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR orange (8039) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep, RAL 2003.

PRECITEĀ®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/mĀ²

PRECITEĀ® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROLOYĀ®

Preliminary

PARA GF 35 FR natural (8038)

PARA GF35 FR(40)

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/mĀ²

AKROLOYĀ® PARA GF 35 FR natural (8038) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROMIDĀ®

Preliminary

B3 GF 40 S1 black (8647)

PA6-I GF40

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/mĀ²

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

111121380

AKROMIDĀ®

B3 GK 30 black (1827)PA6 GB30

AKROMIDĀ® B3 GK 30 black (1827) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

low warpage

Properties

Modulus

4.500MPa

Strength

75MPa

Impact

20kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4500 MPa
2000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
75 MPa
40 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
> 3,5 %
> 25 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
3300 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
110 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
20 kJ/mĀ²
40 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
3 kJ/mĀ²
5 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

358N/30s | conditioned
961N/30s | d.a.m.
90 MPa
180 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
20.000 h
100 Ā°C
90 Ā°C

Vicat softening temperature B50

ISO 306

50Ā°C/50N
205 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,34 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,0 - 2,2 %

Water absorption

ISO 62

23Ā°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,8 - 1,0 %
0,9 - 1,1 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
360 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.