Select your fitting and find the right compound for your intend
AKROMID®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/m²
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 60 1 natural (4775)
PA6 GF60
AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
22.000MPa
260MPa
100kJ/m²
AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
AKROMID®
B3 GF 30 1 L natural (4684)
PA6+PP GF30
AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride
8.500MPa
150MPa
70kJ/m²
AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride
AKROLOY®
PA GF 50 natural (6414)
PA66+PA6I/6T GF50
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
17.000MPa
275MPa
110kJ/m²
AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.
PRECITE®
P3 GF 30 black (6924)
PBT GF 30
PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
10.000MPa
145MPa
68kJ/m²
PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 GF 30 RM-M black (3016)
PA6+X GF30
AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
11.000MPa
165MPa
70kJ/m²
AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
AKROMID®
AKROMID® T91 GF 30 FR natural (8667) is an easy flow, flame retardant and 30% glass fiber reinforced Polyamide 9T with high stiffness and strength. This material is based on the latest flame retardant technology, that is free of red phosphorous, melamine, PFAS and halogenes. This product is characterised by very high flowability for thin walled parts. Due its high melting point and low water uptake it is a perfect candidate for SMT devices.
Features
Properties
10.500MPa
150MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
UL 94
ISO 1183
ISO 1110
ISO 294-4
IEC 60112
IEC 60243
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.