AKROLOY®

PA GF 60 black (6418)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITE®

P3 GF 30 natural (6850)

PBT GF30

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/m²

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMID®

UL

B3 GF 30 FR natural (7458)

PA6 GF30 FR(40)

AKROMID® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

Modulus

10.800MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR natural (7458) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion.

AKROMID®

UL

A3 GF 30 8 HU natural (8102)

PA66 GF30

AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROTEK®

RA GFM 15/25 black (8216)

PA6 (GF15+MD25)

AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

Modulus

8.500MPa

Strength

120MPa

Impact

50kJ/m²

AKROTEK® RA GFM 15/25 black (8216) - PA 6, 15% glass fiber reinforced, 25% mineral filled, radar absorption, 76-81 GHz

AKROMID®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

PRECITE®

P3 GF 30 black (6924)

PBT GF 30

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

19101180

AKROMID®

Preliminary

B3 GF 40 S1 black (8647)PA6-I GF40

EXPERIMENTAL GRADE AKROMID® B3 GF 40 S1 black (8647) is a 40% glass fiber reinforced, impact modified polyamide 6. It is characterised by a high cold impact a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Features

impact modified
reduced density

Properties

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
105 kJ/m²
125 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
26 kJ/m²
38 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,42 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0.25 - 0.45 %
0.7 - 0.9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
100 mm
310 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.