T9 GF 50 black (7601)

PPA GF50

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

17.000MPa

Strength

250MPa

Impact

95kJ/mĀ²

AKROMIDĀ® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

AKROMIDĀ®

A28 LGF 50 9 black (7705)

PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

AKROMIDĀ®

B28 GF 60 1 natural (4775)

PA6 GF60

AKROMIDĀ® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

22.000MPa

Strength

260MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

Preliminary

B3 GF 40 S1 black (8647)

PA6-I GF40

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/mĀ²

AKROMIDĀ® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

UL

A3 GF 30 8 HU natural (8102)

PA66 GF30

AKROMIDĀ® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROMIDĀ®

UL
Preliminary

A3 GF 30 8 HU black (8112)

PA66 GF30

AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

10.500MPa

Strength

200MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROMIDĀ®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

19101180

PRECITEĀ®

P3 GF 30 natural (6850)PBT GF30

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Properties

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
145 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
65 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
11 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
225 Ā°C

General properties

Density

ISO 1183

23Ā°C
1,53 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,2 %

Water absorption

ISO 62

23Ā°C, saturated
0,4 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
> 1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
350 V

Rheological Properties

MVR

ISO 1133

250Ā°C/2,16kg
9 cmĀ³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more