AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A28 LGF 50 9 black (7705)
PA66 LGF50
AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan
18.000MPa
270MPa
95kJ/m²
AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan
AKROMID®
B28 GF 60 1 natural (4775)
PA6 GF60
AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
22.000MPa
260MPa
100kJ/m²
AKROMID® B28 GF 60 1 natural (4775) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow
AKROMID®
B3 GF 40 S1 black (8647)
PA6-I GF40
AKROMID® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry
11.000MPa
175MPa
105kJ/m²
AKROMID® B3 GF 40 S1 black (8647) - 40% glass fiber reinforced PA 6, impact modified, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 30 8 HU natural (8102)
PA66 GF30
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMID®
A3 GF 30 8 HU black (8112)
PA66 GF30
AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU black (8112) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMID®
A3 CGM 10/20 4 black (5870)
PA66 (CF10+GF20)
AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity
14.500MPa
190MPa
65kJ/m²
AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity
AKROMID®
C3 GF 30 8 black (5657)PA66 + PA6 GF30
AKROMID® C3 GF 30 8 black (5657) is 30% glass fiber reinforced PA6.6/6 Blend with average rigidity and strength. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.
Regulatory
Properties
9.400MPa
190MPa
82kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.