PRECITEĀ®

P3 GF 30 black (6924)

PBT GF 30

PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/mĀ²

PRECITEĀ® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROTEKĀ®

PK-VM natural (4774)

PK

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

A28 LGF 50 9 black (7705)

PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

AKROMIDĀ® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

AKROMIDĀ®

C3 GF 30 5 XTC black (4686)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

AKROMIDĀ®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

AKROMIDĀ®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/mĀ²

AKROMIDĀ® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

C3 GF 35 1 black (4668)

PA66+PA6 GF35

AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry

19101180

AKROMIDĀ®

A3 ICF 30 black (5021)PA66 CF30

AKROMIDĀ® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties

Properties

Modulus

24.000MPa

Strength

240MPa

Impact

55kJ/mĀ²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
24000 MPa
15000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
240 MPa
170 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,8 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
22000 MPa
14000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
370 MPa
265 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,5 %
3,5 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
55 kJ/mĀ²
70 kJ/mĀ²
55 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
8 kJ/mĀ²
11 kJ/mĀ²
6 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,06 10ā»ā“/K
0,72 10ā»ā“/K

Thermal conductivity

DIN 52612

0,42 W/mK

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
> 650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
104 ā„¦
104 ā„¦

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more