Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

B3 GF 40 black (6077)

PA6 GF40

AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/m²

AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROLOY®

PA GF 50 natural (6414)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

Modulus

17.000MPa

Strength

275MPa

Impact

110kJ/m²

AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state.

AKROLOY®

PA GF 60 black (6418)

PA66+PA6I/6T GF60

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Modulus

21.000MPa

Strength

275MPa

Impact

100kJ/m²

AKROLOY® PA GF 60 black (6418) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

PRECITE®

P3 GF 30 black (6924)

PBT GF 30

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

68kJ/m²

PRECITE® P3 GF 30 black (6924) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

AKROMID®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/m²

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

AKROMID®

A28 LGF 50 9 black (7705)

PA66 LGF50

AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/m²

AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

19101180

AKROMID®

A3 1 L black (4652)PA66 + PP

AKROMID® A3 1 L black (4652) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
54 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
6,5 kJ/m²
12 kJ/m²
5 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
800 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
2,5 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
29 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.