AKROMID®

NEXT S3 GF 30 S1 black (8887)PA610-I GF30

AKROMID® NEXT S3 GF 30 S1 black (8887) a partially biobased and impact modified PA6.10. With 15% glass fibre reinforcement, the material is suitable for household and industrial applications with high demands on strength, stiffness and impact strength. This sustainable grade is characterised by its low moisture absorption and high chemical resistance compared to classic PA6 and PA 6.

Features

Bio-based
hydrolysis / chemically stabilised
impact modified
reduced moisture

Properties

Modulus

7.800MPa

Strength

135MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

51 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
135 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
25 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
120 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
195 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

General properties

Density

ISO 1183

23°C
1,27 g/cm³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.