Description

AKROMIDĀ®

A3 GM 20/10 4 WIT black (4529)

PA66 (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 GM 20/10 4 WIT black (4529) - 20% glass fibre, 10% glass bead, hydrolysis/chemical, polyamide 6.6, good surface, low warpage

AKROMIDĀ®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMIDĀ® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

AKROMIDĀ®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

AKROTEKĀ®

PK-VM natural (4774)

PK

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

C3 GF 30 5 XTC black (4686)

PA66+PA6 GF30

AKROMIDĀ® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

AKROMIDĀ®

A3 1 S3 black (2768)

PA66+PA6-I

AKROMIDĀ® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.600MPa

Strength

68MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 1 S3 black (2768) - PA66, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

1891080

AKROMIDĀ®

A28 LGF 50 9 black (7705)PA66 LGF50

AKROMIDĀ® A28 LGF 50 9 black (7705) is an easy flowing PA6.6 with 50% long glass fibre reinforcement which leads to an extraordinary high stiffness and strength even at high temperature. The material distinguishes itself due to its isotropic mechanical properties as well as increased creep resistance and higher heat deflection temperature. The excellent fatigue performance, high energy absorption in the event of a crash and low shrinkage make it the product of your choice for technical parts e.g. oil pan.

Features

easy flow
process improved

Properties

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18000 MPa
14200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
210 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
2,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
100 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
45 kJ/mĀ²
45 kJ/mĀ²

Izod impact strength

ISO 180/1A

23Ā°C | d.a.m.
90 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
260 Ā°C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
60 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,25 10ā»ā“/K
0,75 10ā»ā“/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h
150 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,57 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.