B3 1 L ECO black (8969)PA6+PP(REC)

AKROMID® B3 1 L ECO black (8969) is a PA6+PP blend with post consumer recycled content and reduced density. This material is suitable for components where weight reduction is required.

Features

heat stabilised 130
recycled content
reduced density
sustainable
CO2eq reduced

Properties

Modulus

2.500MPa

Strength

60MPa

Impact

180kJ/m²

Sustainability

Recycled content

ISO 14021

Post-consumer (PCR)
> 30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
2500 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
60 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,5 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
≥ 20 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
no break
100

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
4 kJ/m²
2 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Flammability

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General Properties

Density

ISO 1183

23°C
1,04 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Similar products

AKRO Compound Explorer

AKROMID®

B3 ICF 10 1 black (6194)

PA6 CF10

AKROMID® B3 ICF 10 1 black (6194) is a heat stabilised Polyamide 6 with 10% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

8.500MPa

Strength

125MPa

Impact

45kJ/m²

AKROMID®

Preliminary

B3 GF 15 1 L ECO black (8968)

PA6+PP(REC) GF15

AKROMID® B3 GF 15 1 L ECO black (8968) is a PA6+PP blend with post consumer recycled content and reduced density. With 15 % glass fiber reinforcement this material is suitable for components with average strength and stiffness where weight reduction

Modulus

5.500MPa

Strength

100MPa

Impact

54kJ/m²

AKROMID®

Preliminary

B3 GF 30 1 L ECO black (8967)

PA6+PP GF30

AKROMID® B3 GF 30 1 L ECO black (8967) is a PA6+PP blend with post consumer recycled content and reduced density. With 30% glass fiber reinforcement this material is suitable for components with high strength and stiffness where weight reduction is r

Modulus

9.000MPa

Strength

140MPa

Impact

57kJ/m²

PRECITE®

Preliminary

P3 ICF 10 black (6946)

PBT CF10

PRECITE® P3 ICF 10 black (6946) is a PBT reinforced with 10% recycled carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing cl

Modulus

7.500MPa

Strength

100MPa

Impact

30kJ/m²

AKROMID®

Preliminary

B3 ICF 10 AM black (8336)

PA6 CF10

AKROMID® B3 ICF 10 AM black (8336) is a Polyamide 6 with 10% carbon fiber reinforcement, offering high stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. It is suitable for a

Modulus

8.000MPa

Strength

120MPa

Impact

45kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (9172)

PA6 GF30

AKROMID® B3 GF 30 ECO black (9172) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6 with a basic laser markability. The formulation of this sustainable ECO product is partly based on post-consumer recycled feedstock and thus contribute to

Modulus

10.000MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID®

B3 1 L black (4525)

PA6+PP

AKROMID® B3 1 L black (4525) is an unreinforced PA6-PP-blend with reduced density compared to standard PA6. The material can be used where weight and cost reduction is required.

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID®

B3 ICF 20 LF black (6695)

PA6 CF20

AKROMID® B3 ICF 20 LF black (6695) is a high performance Polyamide 6 with 20% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Due

Modulus

15.000MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

Preliminary

P3 ICF 30 black (6948)

PBT CF30

PRECITE® P3 ICF 30 black (6948) is a PBT reinforced with 30% recycled carbon fiber with excellent dimensional stability. Thanks to its low moisture absorption, PRECITE® achieves consistent mechanical and electrical properties, even under changing cl

Modulus

23.500MPa

Strength

175MPa

Impact

50kJ/m²

PRECITE®

Preliminary

E ICF 20 black (7428)

PET CF20

PRECITE® E ICF 20 black (7428) is a medium viscosity polyethylene terephthalate (PET) with 20% recycled carbon fiber. Despite lower density compared to PET with glass fiber reinforcement, the product has very high strength and toughness as well as hi

Modulus

17.000MPa

Strength

180MPa

Impact

41kJ/m²

AKROMID®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMID® B3 GF 30 ECO black (7923) is a 30% glass fibre-reinforced, heat-stabilised polyamide 6. This compound is suitable for technical components in mechanical engineering and automotive industry with demands for high stiffness and strength. The fo

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/m²

AKROMID®

B3 ICF 15 black (5026)

PA6 CF15

AKROMID® B3 ICF 15 black (5026) is a high performance Polyamide 6 with 15% carbon fiber reinforcement, offering medium stiffness and flexural strength. Compared to glass fiber-reinforced PA 6, it provides an optimized strength-to-weight ratio. Thanks

Modulus

11.000MPa

Strength

140MPa

Impact

55kJ/m²