AKROMID®

Preliminary

NEXT 5.6 3 GF 30 FR black (8465)

PA56 GF30 FR(40)

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

Modulus

11.000MPa

Strength

137MPa

Impact

64kJ/m²

AKROMID® NEXT 5.6 3 GF 30 FR black (8465) - PA 5.6, bio-based, HMD-free, flame retardant, 30% GF, high strength, E&E, E-Mobility.

AKROMID®

C3 GF 30 5 XTC black (4686)

PA66+PA6 GF30

AKROMID® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC black (4686) - PA6.6/6 blend, 30% glass fiber reinforced, high heat stabilised, industrial engineering, automotive industry

AKROMID®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/m²

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

AKROMID®

B3 GF 30 6 black (20009)

PA6 GF30

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

10.000MPa

Strength

180MPa

Impact

80kJ/m²

AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A28 LGF 50 9 black (7705)

PA66 LGF50

AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

Modulus

18.000MPa

Strength

270MPa

Impact

95kJ/m²

AKROMID® A28 LGF 50 9 black (7705) - 50% long glass fiber reinforced PA6.6, easy flowing, process improved, low shrinkage, very good fatigue performance, oil pan

AKROMID®

B3 GF 40 black (6077)

PA6 GF40

AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/m²

AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

PRECITE®

P3 GFM 20/10 natural (7627)

PBT (GF20+MD10)

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

Modulus

9.300MPa

Strength

115MPa

Impact

50kJ/m²

PRECITE® P3 GFM 20/10 natural (7627) - PBT, glass fibre and mineral reinforced, very good dimensional stability, good surface.

1891080

AKROMID®

B3 GF 40 5 black (7286)PA6 GF40

AKROMID® B3 GF 40 5 black (7286) is a 40% glass fiber reinforced polyamide 6. It is characterised by a very high stiffness and strength. Furthermore, the material is high heat stabilised and therefore perfectly suitable for technical parts which are used at elevated temperatures in industrial engineering and in the automotive industry. As successor AKROMID® B3 GF 40 5 black (8636) was delevoped, to meet the stringent UV stability requirements for outdoor applications.

Features

heat stabilised 160

Properties

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12500 MPa
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
200 MPa
129 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12300 MPa
7500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
310 MPa
200 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,3 %
5,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
95 kJ/m²
103 kJ/m²
92 kJ/m²
96 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
16 kJ/m²
24 kJ/m²
13 kJ/m²
14 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,45 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Rheological Properties

Flowability

AKRO

2 mm Thickness
480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more