Select your fitting and find the right compound for your intend
AKROMID®
C3 GF 35 1 black (4668)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
200MPa
95kJ/m²
AKROMID® C3 GF 35 1 black (4668) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 30 6 black (20009)
PA6 GF30
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
10.000MPa
180MPa
80kJ/m²
AKROMID® B3 GF 30 6 black (20009) - 30% glass fiber reinforced PA 6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROLOY®
PARA GF 35 FR black (7496)
PARA GF35 FR(40)
AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
14.500MPa
190MPa
55kJ/m²
AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.
AKROMID®
B3 GF 30 RM-M black (3016)
PA6+X GF30
AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
11.000MPa
165MPa
70kJ/m²
AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required
AKROMID®
B3 GF 40 black (6077)
PA6 GF40
AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
13.000MPa
205MPa
110kJ/m²
AKROMID® B3 GF 40 black (6077) - 40% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry
AKROMID®
T9 GF 50 black (7601)
PPA GF50
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
17.000MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 black (7601) is a 50% glass fibre reinforced partially aromatic polyphthalamide with very high stiffness and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
A3 GF 30 8 HU natural (8102)
PA66 GF30
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
10.500MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 8 HU natural (8102) - PA 6.6, 30% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011
AKROMID®
AKROMID® A3 GK 40 1 black (1804) is a heat stabilised PA 6.6 filled with 40% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.
Features
Properties
5.500MPa
95MPa
25kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.