AKROMIDĀ®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMIDĀ® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/mĀ²

AKROMIDĀ® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

AKROMIDĀ®

A3 GF 50 1 natural (1259)

PA66 GF50

AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/mĀ²

AKROMIDĀ® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMIDĀ®

B3 GF 35 natural (2473)

PA6 GF35

AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMIDĀ®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/mĀ²

AKROMIDĀ® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

PRECITEĀ®

P3 GF 30 natural (6850)

PBT GF30

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/mĀ²

PRECITEĀ® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

178980

AKROMIDĀ®

C28 GF 25 FRT grey (8331)PA-Blend

AKROMIDĀ® C28 GF 25 FRT grey (8331) is a 25 % glass fiber reinforced, flame retardant and easy flowing PA blend, colored in grey similar to NCS S 3000 N. The material is based on a flame retardant system that is free of red phosphorus and halogens. This grade is suitable for railroad applications and certified to EN 45545-2 R6 and EN 45545-2 R1. To achieve an excellent surface quality a mould temperature of at least 120Ā°C is necessary.

Features

flame retardant
surface modified
easy flow
public transportation

Regulatory

en45545-2

Properties

Modulus

10.800MPa

Strength

140MPa

Impact

47kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
47 kJ/mĀ²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
238 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,2 10ā»ā“/K
0,66 10ā»ā“/K

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

Burning rate 5V

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
5VA Class
5VA Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 Ā°C
960 Ā°C
960 Ā°C
960 Ā°C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 Ā°C
800 Ā°C
800 Ā°C
850 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Train

EN 45545-2

R1/6/7 HL2

General properties

Density

ISO 1183

23Ā°C
1,44 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
< 0,2 %
0,1 - 0,3 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.