AKROLOY®

PA GF 60 white (7973)PA66+PA6I/6T GF60

AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.

Properties

Modulus

22.000MPa

Strength

270MPa

Impact

85kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
22000 MPa
20000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
240 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,1 %
2,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
85 kJ/m²
90 kJ/m²
70 kJ/m²
80 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
18 kJ/m²
19 kJ/m²
18 kJ/m²
18 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
245 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
240 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
200 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
255 °C

Flammability


Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties


Density

ISO 1183

23°C
1,72 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,2 - 0,4 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.