AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

AKROMID®

A3 GF 50 1 natural (1259)

PA66 GF50

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 natural (1259) - 50% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/m²

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMID®

B3 GF 35 natural (2473)

PA6 GF35

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 30 1 L natural (4684)

PA6+PP GF30

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

8.500MPa

Strength

150MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 1 L natural (4684) - PA6/PP-Blend 30% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

A3 CGM 10/20 4 black (5870)

PA66 (CF10+GF20)

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

Modulus

14.500MPa

Strength

190MPa

Impact

65kJ/m²

AKROMID® A3 CGM 10/20 4 black (5870) - PA6.6, 20% glass fiber, 10% carbon fiber, cooling water, hydrolysis resistant, electrical conductivity

PRECITE®

P3 GF 30 natural (6850)

PBT GF30

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

Modulus

10.000MPa

Strength

145MPa

Impact

65kJ/m²

PRECITE® P3 GF 30 natural (6850) is a 30% glass fibre reinforced, medium viscous polybutylene terephthalate (PBT) with high stiffness and toughness as well as high dimensional stability and chemical resistance.

178980

AKROMID®

Preliminary

A3 GF 30 6 ECO black (8160)PA6.6 GF30

AKROMID® A3 GF 30 6 ECO black (8160) is a 30% glass fibre-reinforced, inorganically heat-stabilised polyamide 6.6. The material is suitable for technical components in mechanical engineering and the automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock (at least 30 weight-% by recipe) and thus contribute to reducing the consumption of valuable raw materials. This type is laser-markable.

Features

heat stabilised 160
laser markable
recycled content

Properties

Modulus

9.000MPa

Strength

150MPa

Impact

50kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9000 MPa
6300 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
150 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7500 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
50 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
7 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
255 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more