AKROMID®

A3 GF 35 3 black (1802)

PA66 GF35

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

180MPa

Impact

50kJ/m²

AKROMID® A3 GF 35 3 black (1802) - 35% glass fiber reinforced PA 6.6, nucleated, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GM 20/10 S1 natural (1217)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 natural (1217) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, adhesion modified, low warpage

AKROMID®

B3 GF 35 natural (2473)

PA6 GF35

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

195MPa

Impact

100kJ/m²

AKROMID® B3 GF 35 natural (2473) - 35% glass fiber reinforced PA 6, technical parts in industrial engineering and automotive industry

AKROMID®

A3 GF 60 1 black (2395)

PA66 GF60

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

Modulus

20.500MPa

Strength

260MPa

Impact

85kJ/m²

AKROMID® A3 GF 60 1 black (2395) - PA6.6, 60% glass fiber, highly reinforced, heat stabilised

AKROMID®

B3 GF 30 RM-M black (3016)

PA6+X GF30

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M black (3016) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

AKROLOY®

PARA GF 35 FR black (7496)

PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

Modulus

14.500MPa

Strength

190MPa

Impact

55kJ/m²

AKROLOY® PARA GF 35 FR black (7496) - PARA, 35% GF, highest modulus and strength, flame retardant, very good flowability, good surface, low creep.

AKROTEK®

PK-VM natural (4774)

PK

AKROTEK® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM natural (4774) - Polyketon, Tribology, friction and wear, chemical resistance

178980

AKROLOY®

Preliminary

PARA GF 35 FR orange (8039)PARA GF35 FR(40)

AKROLOY® PARA GF 35 FR orange (8039) is a flame retardant, 35% glass-fiber reinforced Polyarylamide with highest modulus and strength. The material is based on a flame retardant system that is free of red phosphorus and halogens and is colored in orange similar to RAL 2003. Due to its very good flowability, an improved surface quality is achieved. This grade is also suitable for applications in electrical industries, which need low creep even in conditioned state.

Features

electrically neutral
flame retardant
surface modified
reduced moisture
easy flow
E&E

Properties

Modulus

14.500MPa

Strength

190MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
14500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
190 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
50 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
960 °C
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
825 °C
800 °C
800 °C
825 °C

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,2 - 0,4 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Dielectric strength

IEC 60243

1 mm
36 kV/mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.